Estudo da cinética de polimerização por ATR-FTIR de um sistema adesivo experimental contendo um dendrímero
| dc.contributor.advisor | Cruz, Joana Vasconcelos e | |
| dc.contributor.author | Barbier, Margot Agnès Florence | |
| dc.date.accessioned | 2023-12-04T15:35:45Z | |
| dc.date.available | 2024-10-28T01:30:42Z | |
| dc.date.issued | 2023-10-28 | |
| dc.description | Dissertação para obtenção do grau de Mestre no Instituto Universitário Egas Moniz | pt_PT |
| dc.description.abstract | Objetivos: Estudar a cinética de polimerização (taxa de conversão, taxa de polimerização e tempo de semi-vida) de homopolímeros contendo Bis-GMA, G-IEMA, UDMA, TEGDMA e HEMA, bem como de adesivos (dois comerciais e dois experimentais) usando o ATR-FTIR. Materiais e métodos: Foram formulados cinco homopolímeros, utilizando Bis-GMA, UDMA, TEGDMA, G-IEMA e HEMA, adicionando-lhes CQ e BDA para os tornar fotopolimerizáveis. Para a formulação dos dois adesivos experimentais, o primeiro contém Bis-GMA enquanto o segundo, em vez de Bis-GMA, apresenta G-IEMA com os mesmos componentes. Para o estudo da cinética de polimerização com recurso ao ATR-FTIR, os espetros foram analisados em tempo real antes, durante e depois da fotopolimerização, com uma duração total de 20 minutos. Para cada material foram efetuadas 3 leituras (n=3). A análise dos espectros resultantes e os respetivos cálculos dos parâmetros cinéticos foi realizado com recurso ao software Spectrum TimeBase v. 3.1.4. Para o tratamento estatístico dos dados foram realizados métodos de estatística descritiva e testes de estatística inferencial, utilizando o SPSS v. 26.0 e um nível de significância de 5%. Resultados: Não se verificaram diferenças significativas entre os monómeros em termos de taxa de conversão (p=0,24) e de semi-vida (p=0,15). No entanto, a taxa de polimerização destes monómeros apresentou diferenças altamente significativas entre o UDMA e todos os outros grupos, bem como o G-IEMA e o TEGDMA, que apresentaram taxas de polimerização superiores ao Bis-GMA e ao HEMA (p<0,05). Relativamente aos adesivos, não foram encontradas diferenças significativas na taxa de conversão (p=0,06), na taxa de polimerização (p=0,89) e no tempo de semi-vida (p=0,27). Conclusões: Com base nos resultados, concluiu-se que o G-IEMA parece ser um bom candidato à substituição do Bis-GMA, uma vez que a sua cinética de polimerização é idêntica ou mesmo melhorada. | pt_PT |
| dc.description.abstract | Objectives: Study the polymerisation kinetics (conversion rate, polymerisation rate and halflife time) of homopolymers containing Bis-GMA, G-IEMA, UDMA, TEGDMA and HEMA, as well as adhesives (two commercial and two experimental) using ATR-FTIR. Materials and methods: Five homopolymers were formulated using Bis-GMA, UDMA, TEGDMA, G-IEMA and HEMA, adding CQ and BDA to make them light-curing. For the formulation of the two experimental adhesives, the first contains Bis-GMA while the second, instead of Bis-GMA, contains G-IEMA with the same components. To study polymerisation kinetics with ATR-FTIR, the spectra were analysed in real time before, during and after light-curing, with a total duration of 20 minutes. Three readings (n=3) were taken for each material. The resulting spectra were analysed and the kinetic parameters calculated using the Spectrum TimeBase v. 3.1.4 software. For the statistical treatment of the data, descriptive statistics and inferential statistics tests were carried out using SPSS v. 26.0 and a significance level of 5%. Results: There were no significant differences between the monomers in terms of conversion rate (p=0.24) and half-life (p=0.15). However, the polymerisation rate of these monomers showed highly significant differences between UDMA and all the other groups, as well as GIEMA and TEGDMA, which showed higher polymerisation rates than Bis-GMA and HEMA (p<0.05). As for the adhesives, no significant differences were found in the conversion rate (p=0.06), polymerisation rate (p=0.89) and half-life time (p=0.27). Conclusions: Based on the results, it was concluded that G-IEMA seems to be a good candidate for the substitution of Bis-GMA, since its polymerisation kinetics are identical or even improved. | pt_PT |
| dc.description.abstract | Objectifs : Étudier la cinétique de polymérisation (taux de conversion, taux de polymérisation, temps de semi-vie) d'homopolymères contenant du Bis-GMA, G-IEMA, UDMA, TEGDMA et HEMA, ainsi que d'adhésifs (deux commerciaux et deux expérimentaux) avec l'ATR-FTIR. Matériels et méthodes : Cinq homopolymères ont été formulés à partir de Bis-GMA, UDMA, TEGDMA, G-IEMA et HEMA, avec CQ et BDA pour les rendre photopolymérisables. Concernant la formulation des adhésifs expérimentaux, le premier contient du Bis-GMA tandis que le second, à la place du Bis-GMA, contient du G-IEMA avec les mêmes composants. Pour étudier la cinétique de polymérisation avec l’ATR-FTIR, les spectres ont été analysés en temps réel avant, pendant et après la photopolymérisation, avec une durée totale de 20 minutes. Trois lectures (n=3) ont été effectuées pour chaque matériau. Les spectres obtenus ont été analysés et les paramètres cinétiques calculés à l’aide du logiciel Spectrum TimeBase v. 3.1.4. Pour le traitement statistique des données, des tests statistiques descriptifs et inférentiels ont été effectués avec SPSS v. 26.0 et un niveau de signification de 5 %. Résultats : Il n'y a pas de différence significative entre les monomères pour le taux de conversion (p=0,24) et de semi-vie (p=0,15). Le taux de polymérisation a montré des différences hautement significatives entre l'UDMA et tous les autres groupes, ainsi que le GIEMA et le TEGDMA, qui ont des taux de polymérisation plus élevés que le Bis-GMA et l'HEMA (p<0,05). Pour les adhésifs, aucune différence significative n'a été trouvée concernant le taux de conversion (p=0,06), taux de polymérisation (p=0,89) et temps de semi-vie (p=0,27). Conclusions : Sur la base des résultats, il a été conclu que le G-IEMA semble être un bon candidat pour la substitution du Bis-GMA, puisque sa cinétique de polymérisation est identique voir améliorée. | pt_PT |
| dc.identifier.tid | 203402219 | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10400.26/48204 | |
| dc.language.iso | por | pt_PT |
| dc.subject | Fotopolimerização | pt_PT |
| dc.subject | Adesivo | pt_PT |
| dc.subject | G-IEMA | pt_PT |
| dc.subject | Cinética de polimerização | pt_PT |
| dc.title | Estudo da cinética de polimerização por ATR-FTIR de um sistema adesivo experimental contendo um dendrímero | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestrado Integrado em Medicina Dentária | pt_PT |