Additive manufacturing of rice husk filled PLA composites: development and characterization

dc.contributor.advisorPina, Célio
dc.contributor.advisorMarques, Ana Clara
dc.contributor.authorPereira, Daniel Alexandre Feliciano
dc.date.accessioned2023-01-04T10:48:24Z
dc.date.available2023-01-04T10:48:24Z
dc.date.issued2022-12
dc.description.abstractThe number of published scientific papers about natural fibers as a filler to produce composite filaments for additive manufacturing (AM) has increased in recent years. The aim of this thesis is to develop and characterize rice husk filled PLA composites obtained by AM. Thus, rice husks (RH) were blended with PLA (IngeoTM Biopolymer 4043D) to produce natural fiber filled polymer (NFFP) filaments for AM with fiber amounts between 5 and 20 wt.%. Raw materials, filaments produced and printed parts were characterized. The results showed that the filaments with a fiber content above 15 wt.% were not printable. Adding RH fibers to PLA negatively affected the mechanical strength, water absorption and densities on printed parts, mainly due to high variation in the filament diameter.pt_PT
dc.description.abstractO número de artigos científicos publicados sobre fibras naturais como enchimento na produção de filamentos compósitos para fabrico aditivo (FA) tem aumentado nos últimos anos. O objetivo desta tese foi desenvolver e caracterizar compósitos de PLA e casca de arroz obtidos por FA. Assim, cascas de arroz (CA) foram misturadas com PLA (IngeoTM Biopolymer 4043D) para produzir filamentos de polímero preenchido com fibra natural (PPFN) para FA, com quantidades de fibra a variar entre 5 e 20% em peso. Matérias-primas, filamentos produzidos e peças impressas foram caracterizados. Os resultados mostraram que os filamentos com um conteúdo em fibra superior a 15% em peso não eram imprimíveis. Além disso, adicionar fibras de CA ao PLA afetou negativamente a resistência mecânica, absorção de água e densidades das peças impressas, principalmente devido à variação no diâmetro do filamento.pt_PT
dc.identifier.tid202911241pt_PT
dc.identifier.urihttp://hdl.handle.net/10400.26/42950
dc.language.isoengpt_PT
dc.subjectRice huskpt_PT
dc.subjectNatural fiber-filled polymerpt_PT
dc.subjectAdditive Manufacturingpt_PT
dc.subjectPLApt_PT
dc.subjectCasca de arrozpt_PT
dc.subjectPolímero com enchimento de fibra naturalpt_PT
dc.subjectFabrico aditivopt_PT
dc.titleAdditive manufacturing of rice husk filled PLA composites: development and characterizationpt_PT
dc.typemaster thesis
dspace.entity.typePublication
rcaap.rightsopenAccesspt_PT
rcaap.typemasterThesispt_PT
thesis.degree.grantorInstituto Politécnico de Setúbal
thesis.degree.nameMaster’s dissertation in Production Engineeringpt_PT

Files

Original bundle
Now showing 1 - 1 of 1
Loading...
Thumbnail Image
Name:
Daniel_Pereira_Thesis_201401557_Final.pdf
Size:
5.26 MB
Format:
Adobe Portable Document Format
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.85 KB
Format:
Item-specific license agreed upon to submission
Description: