Publicação
O efeito de bebidas estimulantes na resistência à flexão de resinas compostas universais : estudo in vitro
| dc.contributor.advisor | Azul, Ana Mano | |
| dc.contributor.advisor | Portugal, Jaime | |
| dc.contributor.author | Pereira, Maria Margarida Rebelo de Andrade da Câmara | |
| dc.date.accessioned | 2026-01-20T10:36:43Z | |
| dc.date.available | 2026-01-20T10:36:43Z | |
| dc.date.issued | 2025-11-22 | |
| dc.description | Dissertação para obtenção do grau de Mestre no Instituto Universitário Egas Moniz | |
| dc.description.abstract | Objetivos: Avaliar o efeito de diferentes bebidas estimulantes na resistência à flexão de três resinas compostas – uma multicromática (Filtek™Z250 - FZ) e duas monocromáticas de conceito simplificado (ONEshade – OS e Filtek Easy Match - FEM) – de modo a compreender a influência destas soluções no desempenho mecânico. Materiais e Métodos: Foram preparados 150 espécimes paralelepipédicos (25×2×2 mm), 50 de cada resina composta, segundo a norma ISO 4049:2019. Os espécimes foram distribuídos por cinco grupos (n=10) de acordo com a solução de imersão: água destilada (controlo), café, chá, Coca-Cola® e Red Bull®. Ao longo de 14 dias, cada espécime foi imerso diariamente durante 5 minutos, duas vezes por dia, na respetiva solução; entre imersões e durante a restante armazenagem, os espécimes permaneceram em água destilada a 37±1 °C. Após o período de imersão, foi realizado ensaio de flexão em três pontos numa máquina universal de ensaios (Instron 4502), sendo os valores de resistência à flexão calculados automaticamente pelo software do equipamento. Os dados foram analisados com nível de significância de 5% (α=0,05). Resultados: A ANOVA a duas vias indicou efeito significativo de Resina e de Bebida, sem interação Resina x Bebida. Pelo teste de Tukey HSD, verificou-se resistência inferior da FEM, enquanto FZ e OS não diferiram entre si, FEM < (FZ = OS). Nas comparações dirigidas ao controlo (Dunnett), apenas o chá apresentou redução significativa face à água destilada; café, Coca-Cola® e Red Bull® não diferiram do controlo. Conclusão: Entre os fatores estudados, o tipo de resina foi determinante para a resistência à flexão, e o efeito das bebidas foi modesto, com redução significativa apenas para o chá. As resinas universais monocromáticas testadas evidenciaram comportamento mecânico favorável, apoiando a sua utilização clínica em restaurações diretas, com a ressalva de aconselhamento em contextos de consumo frequente de chá. | por |
| dc.description.abstract | Objectives: To evaluate the effect of different stimulant beverages on the flexural strength of three resin composites—one multishade (Filtek™ Z250) and two simplified single-shade materials (ONEshade and Filtek Easy Match) —to understand how these solutions influence mechanical performance. Materials and Methods: A total of 150 bar-shaped specimens (25 × 2 × 2 mm), 50 per composite, were prepared according to ISO 4049:2019. Specimens were allocated to five groups (n=10) by immersion solution: distilled water (control), coffee, tea, Coca-Cola®, and Red Bull®. Over 14 days, each specimen was immersed twice daily for 5 minutes in its assigned solution; between immersions and during storage, specimens were kept in distilled water at 37±1 °C. Flexural strength was measured using a three-point bending test on a universal testing machine (Instron 4502), with values calculated by the equipment software. The significance level was set at α=0.05. Results: Two-way ANOVA showed significant effects of Composite and Beverage, with no Composite × Beverage interaction. Tukey HSD indicated lower resistance for FEM, while FZ and OS did not differ, i.e., FEM < (FZ = OS). In Dunnett’s comparisons versus control, only tea showed a significant reduction; coffee, Coca-Cola®, and Red Bull® did not differ from distilled water. Conclusions: Among the studied factors, composite type was the main determinant of flexural strength, while beverage effects were modest, with a significant decrease only for tea. The tested single-shade universal composites showed favorable mechanical behavior, supporting their clinical use in direct restorations, with cautionary advice in patients who frequently consume tea. | eng |
| dc.identifier.tid | 204087694 | |
| dc.identifier.uri | http://hdl.handle.net/10400.26/61011 | |
| dc.language.iso | por | |
| dc.rights.uri | http://creativecommons.org/licenses/by/4.0/ | |
| dc.subject | Resistência à flexão | |
| dc.subject | Resinas compostas | |
| dc.subject | Resinas universais | |
| dc.subject | Bebidas estimulantes | |
| dc.title | O efeito de bebidas estimulantes na resistência à flexão de resinas compostas universais : estudo in vitro | por |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| thesis.degree.name | Mestrado Integrado em Medicina Dentária |
Ficheiros
Principais
1 - 1 de 1
Miniatura indisponível
- Nome:
- Pereira, Maria Margarida Rebelo de Andrade da Camara.pdf
- Tamanho:
- 2.15 MB
- Formato:
- Adobe Portable Document Format
Licença
1 - 1 de 1
Miniatura indisponível
- Nome:
- license.txt
- Tamanho:
- 1.85 KB
- Formato:
- Item-specific license agreed upon to submission
- Descrição: