Estudo in vitro da resistência adesiva à dentina utilizando um adesivo universal com a técnica selective dentin etching após envelhecimento térmico
| dc.contributor.advisor | Costa, Joana Almeida e | |
| dc.contributor.advisor | Chasqueira, Ana Filipa | |
| dc.contributor.author | Barrote, Marta Isabel Vieira | |
| dc.date.accessioned | 2024-01-11T10:20:08Z | |
| dc.date.embargo | 2026-11-25 | |
| dc.date.issued | 2023-11-25 | |
| dc.description | Dissertação para obtenção do grau de Mestre no Instituto Universitário Egas Moniz | pt_PT |
| dc.description.abstract | Objetivo: Avaliar in vitro a resistência adesiva à dentina por microtração quando o adesivo OptiBond™ Universal® é aplicado numa estratégia adesiva selective dentin etching após envelhecimento térmico e realizar uma análise ultramorfológica através de microscopia eletrónica de varrimento. Materiais e métodos: Foram usados trinta dentes molares humanos definitivos hígidos extraídos. Após simulação da smear layer, os dentes foram aleatoriamente distribuídos por três grupos experimentais (n = 10): Grupo SE (controlo) – aplicação de OptiBond™ Universal® segundo self-etch; Grupo SDE1 – aplicação de OptiBond™ Universal® pela técnica selective dentin etching (aplicação de ácido ortofosfórico 37 % durante 3 s); Grupo SDE3 – aplicação de três camadas de OptiBond™ Universal® pela técnica selective dentin etching. Após aplicação da resina composta, os dentes foram submetidos a 10 000 ciclos de termociclagem (5-55 ºC) e posteriormente seccionados em palitos com secção transversal de 1 mm2 para serem submetidos a forças de tração numa máquina de testes universal (0,5 mm/min; 1 kN). A superfície de fratura de cada palito foi observada e a falha foi classificada. Os resultados foram analisados estatisticamente com ANOVA one-way (α= 0,05). Um palito por grupo foi selecionado aleatoriamente para ser observado por microscopia. Resultados: Não foram encontradas diferenças estatisticamente significativas (p > 0,05) nos valores de resistência adesiva à microtração entre os três grupos experimentais. A maioria das falhas foi adesiva e as imagens de microscopia mostraram uma camada híbrida uniforme e íntegra em todos os grupos. Conclusões: A aplicação de Optibond™ Universal® com uma estratégia adesiva selective dentin etching não afetou negativamente a adesão à dentina após termociclagem. | pt_PT |
| dc.description.abstract | Objectives: Evaluate in vitro the microtensile bond strength to dentin with OptiBond™ Universal® adhesive applied using a selective dentin etching adhesive strategy after thermal aging and to perform an ultramorphological analysis using scanning electron microscopy. Materials and methods: Thirty extracted healthy human permanent molar were used. After simulating the smear layer, the teeth were randomly distributed into three experimental groups (n = 10): SE (control) group – application of OptiBond™ Universal® according to self-etch; SDE1 group – application of OptiBond™ Universal using the selective dentin etching technique (application of 37 % orthophosphoric acid for 3 s); SDE3 group – application of three layers of OptiBond™ Universal® using the selective dentin etching technique. After application of the composite resin, the teeth were subjected to 10 000 thermocycles (5-55 ºC) and then cut into beams of 1 mm2 crosssection and subjected to microtensile forces in a universal testing machine (0.5 mm/min; 1 kN). The fractured surface of each toothpick was observed, and the failure was classified. The results were statistically analyzed with ANOVA one-way (α = 0.05). One toothpick per group was randomly selected for microscopic observation. Results: No statistically significant differences (p > 0.05) were found in the microtensile bond strength values between the three experimental groups. Most failures were adhesive and SEM images showed a uniform and intact hybrid layer in all groups. Conclusions: The application of OptiBond™ Universal® with a selective dentin etching adhesive strategy did not negatively affect dentin adhesion after thermocycling. | pt_PT |
| dc.identifier.tid | 203431693 | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10400.26/48828 | |
| dc.language.iso | por | pt_PT |
| dc.rights.uri | http://creativecommons.org/licenses/by/4.0/ | pt_PT |
| dc.subject | Selective dentin etching | pt_PT |
| dc.subject | Adesivos universais | pt_PT |
| dc.subject | Adesão | pt_PT |
| dc.subject | Resistência adesiva | pt_PT |
| dc.subject | Termociclagem | pt_PT |
| dc.title | Estudo in vitro da resistência adesiva à dentina utilizando um adesivo universal com a técnica selective dentin etching após envelhecimento térmico | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | embargoedAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestrado Integrado em Medicina Dentária | pt_PT |