Percorrer por autor "Marques, Duarte"
A mostrar 1 - 2 de 2
Resultados por página
Opções de ordenação
- Comparative analysis of endodontic 0.15 stainless-steel K-files : exploring design, composition, and mechanical performancePublication . Baruwa, Abayomi Omokeji; Chasqueira, Filipa; Arantes-Oliveira, Sofia; Caramês, João; Marques, Duarte; Portugal, Jaime; Martins, Jorge N. R.To establish a glide path, smaller files (up to size 0.15) with tapers of 2% are commonly used as pathfinding files. They pre-shape the root canal space before transitioning to larger taper endodontic instruments, aiming to prevent procedural errors. This study aimed to compare the design, metal wire composition, and mechanical characteristics of seven different ISO size 15 stainless-steel hand files (K-File and C-File+). Ninety-one new stainless-steel ISO 15 K-files were mechanically tested. All files were inspected for deformations before the assessment. Dental operating microscope, scanning electron microscope (SEM), and optical microscope analyses were conducted on four randomly selected instruments from each group, and two instruments per group underwent an energy-dispersive X-ray spectroscopy (EDS) analysis. Buckling mechanical tests were performed using an Instron universal testing machine, and microhardness was assessed using a Vickers hardness tester. The statistical analysis employed the nonparametric Mood’s median test, with a significance level set at 0.05. The instrument design analysis unveiled variations in the active blade area length and the number of spirals, while maintaining consistent cross-sections and symmetrical blades. Distinct tip geometries and surface irregularities were observed. While the energy-dispersive X-ray spectroscopy confirmed similar compositions, the buckling strength and microhardness values exhibited variability across for all tested files. Notably, the Dentsply ReadySteel C-File+ recorded the highest buckling value (2.10 N), and the Dentsply ReadySteel K-File exhibited the lowest (1.00 N) (p < 0.05). Moreover, the Dentsply ReadySteel K-File recorded the highest microhardness value (703 HVN), while the SybronEndo Triple-Flex had the lowest (549 HVN) (p < 0.05). While similarities in cross-section design and metal wire composition were noted among the files, variations in the number of spirals and mechanical performance were also observed. Thus, all of these factors should be considered when selecting suitable files for an efficient root canal treatment.
- Comparative analysis of endodontic ISO size 06, 08, and 10 stainless steel K-files used for glide path proceduresPublication . Baruwa, Abayomi Omokeji; Chasqueira, Filipa; Arantes-Oliveira, Sofia; Caramês, João; Marques, Duarte; Portugal, Jaime; Martins, Jorge N. R.Small-sized stainless steel hand files are conventionally employed in root canal treatment procedures for canal scouting and for glide path establishment, owing to their superior flexibility and proficiency in navigating confined spaces. Given the diversity of brands available in the market, there exists potential variability in their physical characteristics, thereby influencing clinical performance. Consequently, this study aims to conduct a comparative analysis of the design, metallurgy, and mechanical characteristics among seven stainless steel hand file brands across ISO sizes 06, 08, and 10. A total of 315 new 25 mm length stainless steel hand files with apical sizes of 0.06, 0.08, and 0.10 from seven distinct brands were included in the study. A meticulous inspection of all instruments was undertaken to identify any structural deformations that might render them ineligible for the study. The design inspection involved the random selection of instruments from each group, which were examined under various microscopes, including a dental operating microscope, optical microscope, and scanning electron microscope. Furthermore, two instruments from each group underwent energy-dispersive X-ray spectroscopy analysis for elemental composition documentation. Mechanical tests were conducted to evaluate the instruments’ resistance to lateral deformation (buckling) and their microhardness. Statistical analysis was executed using the nonparametric Mood’s median test, with a predetermined significance level of 0.05. Regarding the instruments design, all files exhibited an active blade length ranging from 16 to 17 mm. However, variations were observed in the number of spirals, tip designs, and sizes, with the API K-File notably larger in sizes 0.06 and 0.08 compared to the other instruments. Despite uniform elements composition, differences in geometric features and mechanical properties were evident. Concerning buckling strength, the API K-File demonstrated superior performance across all tested sizes, while the Dentsply ReadySteel, SybronEndo, and Mani K-Files exhibited lower results (p < 0.05). In microhardness assessments, both the API and Oro K-Files displayed the lowest outcomes, with medians of 531 HVN and 532 HVN, respectively, whereas the SybronEndo K-File exhibited the highest microhardness (657 HVN). Despite similar metallurgical composition, the observed distinctions in geometric features and mechanical properties underscore the impact of the manufacturing process on the characteristics of glide path stainless steel endodontic files. These disparities may ultimately influence their clinical performance.