Estudo da incorporação de diferentes iões metálicos em esmalte humano fluoretado por avaliação da microdureza de superfície
| dc.contributor.advisor | Manso, Ana Cristina | |
| dc.contributor.advisor | Ascenso, Carla | |
| dc.contributor.advisor | Carmo, Joana do | |
| dc.contributor.author | Mira, Alice Maria Aldeagas | |
| dc.date.accessioned | 2021-02-11T16:52:50Z | |
| dc.date.available | 2022-12-01T01:30:24Z | |
| dc.date.issued | 2020-12 | |
| dc.description | Dissertação para obtenção do grau de Mestre no Instituto Universitário Egas Moniz | pt_PT |
| dc.description.abstract | Objetivo: Medir e comparar a microdureza de superfície de esmalte após a incorporação de diferentes catiões e de flúor na hidroxiapatite. Materiais e métodos: 18 molares humanos, íntegros, a partir dos quais foram obtidos 70 fragmentos de esmalte, aleatoriamente divididos em 7 grupos de estudo (A, B, C, D, E, F e G). Em todos os grupos, exceto no A, foi aplicado um verniz de fluoreto de sódio a 5% (Profluorid® Varnish, VOCO, Cuxhaven, Alemanha). O grupo B foi seguidamente imerso em água destilada e os grupos C a G em soluções de saliva artificial diferentes, por um período de 6 dias e com renovação diária: C, saliva artificial isenta de cloreto de cálcio; D, saliva artificial com cloreto de cálcio; E, saliva artificial com cloreto de estrôncio em substituição do cloreto de cálcio; F, saliva artificial com cloreto de magnésio em substituição do cloreto de cálcio e G, saliva artificial com cloreto de zinco em substituição do cloreto de cálcio. Todas os grupos foram avaliados quanto à microdureza de superfície através do teste de Vickers. Os resultados foram tratados estatisticamente pela aplicação do teste ANOVA a um fator com intervalo de confiança de 95% e pelo teste de Bonferroni (software SPSS Statistics versão 24.0 (IBM, Chicago, EUA). Resultados: O grupo B foi o único que não apresentou mineralização e exibiu um valor de microdureza de 472±6 HV (p<0,05), não diferindo estatisticamente do grupo A (controlo) 466±7 HV (p<0,05). Os restantes grupos apresentaram como valores de microdureza, C: 485±4 HV; D: 572±7 HV; E: 517±5 HV; F: 531±6 HV; G: 504±8 HV. Para os 7 grupos foram obtidos valores de p>(0,05). Conclusões: Tanto o estrôncio, como o magnésio ou o zinco originaram valores médios de microdureza de esmalte indicativos de ter acontecido mineralização, porém os resultados foram sempre menores aos causados pelo cálcio. | pt_PT |
| dc.description.abstract | Objectives: Measure and compare the microhardness of enamel surface after the incorporation of different cations and fluoride in hydroxyapatite. Materials and methods: 18 human molars, intact, from which 70 enamel fragments were obtained, randomly divided into 7 study groups (A, B, C, D, E, F and G). In all groups, except A, a 5% sodium fluoride varnish (Profluorid® Varnish, VOCO, Cuxhaven, Germany) was applied. Group B was subsequently immersed in distilled water and groups C to G in different artificial saliva solutions, for a period of 6 days and with daily renewal: C, calcium chloride free artificial saliva; D, calcium chloride free artificial saliva; E, strontium chloride substituted artificial saliva; F, magnesium chloride substituted artificial saliva and G, zinc chloride substituted artificial saliva. All groups were evaluated for surface microhardness using the Vickers test. The results were treated statistically by applying the ANOVA test to a 95% confidence interval factor and the Bonferroni test (SPSS Statistics software version 24.0 (IBM, Chicago, EUA).Results: Group B was the only one that did not show mineralization and showed a microhardness value of 472±6 HV (p<0.05), not differing statistically from group A (control) 466±7 HV (p<0.05). The remaining groups showed as microhardness values, C: 485±4 HV; D: 572±7 HV; E: 517±5 HV; F: 531±6 HV; G: 504±8 HV. For the 7 groups p>(0.05) values were obtained. Conclusions: Both strontium, magnesium and zinc originated average values of enamel microhardness indicative of mineralization, but the results were always lower than those caused by calcium. | pt_PT |
| dc.identifier.tid | 202604217 | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10400.26/35401 | |
| dc.language.iso | por | pt_PT |
| dc.subject | Esmalte | pt_PT |
| dc.subject | Iões divalentes | pt_PT |
| dc.subject | Mineralização | pt_PT |
| dc.subject | Microdureza | pt_PT |
| dc.title | Estudo da incorporação de diferentes iões metálicos em esmalte humano fluoretado por avaliação da microdureza de superfície | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestrado Integrado em Medicina Dentária | pt_PT |