Produção e caracterização de compósitos de matriz epóxi com fibras de conteira e de sisal

2021-09Dissertação de mestrado Acesso aberto
Ver registo simples
dc.contributor.advisorPina, Célio
dc.contributor.advisorMarat-Mendes, Rosa
dc.contributor.authorFreitas, João Rui Aguiar de
dc.date.accessioned2022-01-04T10:47:56Z
dc.date.available2025-01-31T01:30:23Z
dc.date.issued2021-09
dc.description.abstractExiste uma grande necessidade na procura de materiais inovadores, económicos e sustentáveis. O desenvolvimento de materiais mais resistentes, duráveis e com elevada ductilidade é possível utilizando a incorporação de fibras, tais como as naturais, nos materiais compósitos. Assim, o presente trabalho teve como objetivo produzir e caracterizar compósitos com fibra de conteira e fibra de sisal, numa matriz de epóxi. Para tal, foram fabricados compósitos com percentagens de fibra a variar entre 2.5% a 10% em peso, com um tamanho de fibra de 6 mm. Estas fibras foram submetidas a um tratamento alcalino com NaOH, para garantir uma melhor adesão das fibras à matriz. Para a caracterização dos materiais, recorreu- se ao método de Arquimedes, à macroscopia e microscopia eletrónica de varrimento e as propriedades mecânicas foram obtidas através de ensaios de dureza e de tração. Os resultados mostraram uma variação pouco significativa na densidade dos compósitos com o aumento da quantidade de fibra incorporada, e também uma diminuição da resistência à tração, ductilidade e tenacidade à fratura dos materiais. Por outro lado, com este aumento da quantidade registou-se um aumento do módulo de elasticidade, assim como um aumento da dureza dos materiais compósitos. Em suma a adição de fibra aumenta de forma significativa a estabilidade dimensional dos materiais, contudo conduz a uma redução da resistência à tração.pt_PT
dc.description.abstractThere is a great need in the search for innovative, economical and sustainable materials. The development of materials more resistant, durable and with high ductility is possible using the incorporation of fibers, such as natural fibers, in composite materials. Thus, the present work aimed to produce and characterise composites with conteira fibre and sisal fibre, in an epoxy matrix. For this, composites with fibre percentages varying between 2.5% and 10% in weight, with a fibre size of 6 mm, were fabricated. These fibres were submitted to an alkaline treatment with NaOH, to guarantee a better adhesion of the fibres to the matrix. For the characterisation of the materials, the Archimedes method, macroscopy and scanning electron microscopy were used and the mechanical properties were obtained through hardness and tensile tests. The results showed a small significant variation in the density of the composites with the increase of the amount of fibre incorporated, and also a decrease in the tensile strength, ductility and fracture toughness of the materials. On the other hand, with this increase in the amount there was an increase in the modulus of elasticity, as well as an increase in the hardness of the composite materials. In summary, the addition of fibre significantly increases the dimensional stability of the materials, but leads to a reduction in tensile strength.pt_PT
dc.identifier.tid202790622pt_PT
dc.identifier.urihttp://hdl.handle.net/10400.26/38562
dc.language.isoporpt_PT
dc.subjectCompósitospt_PT
dc.subjectResina Epóxipt_PT
dc.subjectFibras de Conteirapt_PT
dc.subjectFibras de Sisal e Ensaios Mecânicospt_PT
dc.subjectCompositespt_PT
dc.subjectEpoxy Resinpt_PT
dc.subjectConteira Fiberspt_PT
dc.subjectSisal Fibers and Mechanical Testingpt_PT
dc.titleProdução e caracterização de compósitos de matriz epóxi com fibras de conteira e de sisalpt_PT
dc.typemaster thesis
dspace.entity.typePublication
rcaap.rightsopenAccesspt_PT
rcaap.typemasterThesispt_PT
thesis.degree.grantorInstituto Politécnico de Setúbal
thesis.degree.nameMestradso em Engenharia de Produçãopt_PT

Ficheiros

Principais
A mostrar 1 - 1 de 1
Miniatura
Nome:
Dissertação-João Freitas-201500420-MEP-Versão Final.pdf
Tamanho:
4.23 MB
Formato:
Adobe Portable Document Format
Ver/Abrir

Coleções

IPS - ESTS - BIBLIOTECA - Dissertações de mestrado